Influence of water storage on fatigue strength of self-etch adhesives

Toshiki Takamizawa, Wayne W. Barkmeier, Akimasa Tsujimoto, Donal D. Scheidel, Hidehiko Watanabe, Robert L. Erickson, Mark A. Latta, Masashi Miyazaki

Research output: Contribution to journalArticle

27 Citations (Scopus)

Abstract

Objectives: The purpose of this study was to determine enamel and dentin bond durability after long-term water storage using self-etch adhesives. Methods: Two single step self-etch adhesives (SU, Scotchbond Universal and GB, G-[U+04D5]nial Bond) and a two-step self-etch adhesive (OX, OptiBond XTR) were used. The shear bond strength (SBS) and shear fatigue strength (FS) of the enamel and dentin were obtained with and without phosphoric acid pre-etching prior to application of the adhesives. The specimens were stored in distilled water at 37. °C for 24. h, 6 months, and one year. A staircase method was used to determine the FS using a frequency of 10. Hz for 50,000 cycles or until failure occurred. Results: The SBS and FS of enamel bonds were significantly higher with pre-etching, when compared to no pre-etching for the same water storage period. The FS of dentin bonds with pre-etching tended to decrease relative to no pre-etching at the same storage period. For the one year storage period, SU and GB with pre-etching showed significantly lower FS values than the groups without pre-etching. Conclusions: The influence of water storage on FS of the self-etch adhesives was dependent on the adhesive material, storage period and phosphoric acid pre-etching of the bonding site. Clinical significance: Phosphoric acid pre-etching of enamel improves the effectiveness of self-etch adhesive systems. Inadvertent contact of phosphoric acid on dentin appears to reduce the ability of self-etch adhesives to effectively bond resin composite materials.

Original languageEnglish (US)
JournalJournal of Dentistry
DOIs
StateAccepted/In press - May 27 2015
Externally publishedYes

Fingerprint

Adhesives
Fatigue
Dentin
Dental Enamel
Water
Shear Strength
Composite Resins
phosphoric acid

Keywords

  • Fatigue strength
  • Long-term water storage
  • Phosphoric acid pre-etching
  • Self-etch adhesive

ASJC Scopus subject areas

  • Dentistry(all)

Cite this

Takamizawa, T., Barkmeier, W. W., Tsujimoto, A., Scheidel, D. D., Watanabe, H., Erickson, R. L., ... Miyazaki, M. (Accepted/In press). Influence of water storage on fatigue strength of self-etch adhesives. Journal of Dentistry. https://doi.org/10.1016/j.jdent.2015.10.018

Influence of water storage on fatigue strength of self-etch adhesives. / Takamizawa, Toshiki; Barkmeier, Wayne W.; Tsujimoto, Akimasa; Scheidel, Donal D.; Watanabe, Hidehiko; Erickson, Robert L.; Latta, Mark A.; Miyazaki, Masashi.

In: Journal of Dentistry, 27.05.2015.

Research output: Contribution to journalArticle

Takamizawa, T, Barkmeier, WW, Tsujimoto, A, Scheidel, DD, Watanabe, H, Erickson, RL, Latta, MA & Miyazaki, M 2015, 'Influence of water storage on fatigue strength of self-etch adhesives', Journal of Dentistry. https://doi.org/10.1016/j.jdent.2015.10.018
Takamizawa, Toshiki ; Barkmeier, Wayne W. ; Tsujimoto, Akimasa ; Scheidel, Donal D. ; Watanabe, Hidehiko ; Erickson, Robert L. ; Latta, Mark A. ; Miyazaki, Masashi. / Influence of water storage on fatigue strength of self-etch adhesives. In: Journal of Dentistry. 2015.
@article{77baa2b30eec4b07ac34d0fd36b60548,
title = "Influence of water storage on fatigue strength of self-etch adhesives",
abstract = "Objectives: The purpose of this study was to determine enamel and dentin bond durability after long-term water storage using self-etch adhesives. Methods: Two single step self-etch adhesives (SU, Scotchbond Universal and GB, G-[U+04D5]nial Bond) and a two-step self-etch adhesive (OX, OptiBond XTR) were used. The shear bond strength (SBS) and shear fatigue strength (FS) of the enamel and dentin were obtained with and without phosphoric acid pre-etching prior to application of the adhesives. The specimens were stored in distilled water at 37. °C for 24. h, 6 months, and one year. A staircase method was used to determine the FS using a frequency of 10. Hz for 50,000 cycles or until failure occurred. Results: The SBS and FS of enamel bonds were significantly higher with pre-etching, when compared to no pre-etching for the same water storage period. The FS of dentin bonds with pre-etching tended to decrease relative to no pre-etching at the same storage period. For the one year storage period, SU and GB with pre-etching showed significantly lower FS values than the groups without pre-etching. Conclusions: The influence of water storage on FS of the self-etch adhesives was dependent on the adhesive material, storage period and phosphoric acid pre-etching of the bonding site. Clinical significance: Phosphoric acid pre-etching of enamel improves the effectiveness of self-etch adhesive systems. Inadvertent contact of phosphoric acid on dentin appears to reduce the ability of self-etch adhesives to effectively bond resin composite materials.",
keywords = "Fatigue strength, Long-term water storage, Phosphoric acid pre-etching, Self-etch adhesive",
author = "Toshiki Takamizawa and Barkmeier, {Wayne W.} and Akimasa Tsujimoto and Scheidel, {Donal D.} and Hidehiko Watanabe and Erickson, {Robert L.} and Latta, {Mark A.} and Masashi Miyazaki",
year = "2015",
month = "5",
day = "27",
doi = "10.1016/j.jdent.2015.10.018",
language = "English (US)",
journal = "Journal of Dentistry",
issn = "0300-5712",
publisher = "Elsevier BV",

}

TY - JOUR

T1 - Influence of water storage on fatigue strength of self-etch adhesives

AU - Takamizawa, Toshiki

AU - Barkmeier, Wayne W.

AU - Tsujimoto, Akimasa

AU - Scheidel, Donal D.

AU - Watanabe, Hidehiko

AU - Erickson, Robert L.

AU - Latta, Mark A.

AU - Miyazaki, Masashi

PY - 2015/5/27

Y1 - 2015/5/27

N2 - Objectives: The purpose of this study was to determine enamel and dentin bond durability after long-term water storage using self-etch adhesives. Methods: Two single step self-etch adhesives (SU, Scotchbond Universal and GB, G-[U+04D5]nial Bond) and a two-step self-etch adhesive (OX, OptiBond XTR) were used. The shear bond strength (SBS) and shear fatigue strength (FS) of the enamel and dentin were obtained with and without phosphoric acid pre-etching prior to application of the adhesives. The specimens were stored in distilled water at 37. °C for 24. h, 6 months, and one year. A staircase method was used to determine the FS using a frequency of 10. Hz for 50,000 cycles or until failure occurred. Results: The SBS and FS of enamel bonds were significantly higher with pre-etching, when compared to no pre-etching for the same water storage period. The FS of dentin bonds with pre-etching tended to decrease relative to no pre-etching at the same storage period. For the one year storage period, SU and GB with pre-etching showed significantly lower FS values than the groups without pre-etching. Conclusions: The influence of water storage on FS of the self-etch adhesives was dependent on the adhesive material, storage period and phosphoric acid pre-etching of the bonding site. Clinical significance: Phosphoric acid pre-etching of enamel improves the effectiveness of self-etch adhesive systems. Inadvertent contact of phosphoric acid on dentin appears to reduce the ability of self-etch adhesives to effectively bond resin composite materials.

AB - Objectives: The purpose of this study was to determine enamel and dentin bond durability after long-term water storage using self-etch adhesives. Methods: Two single step self-etch adhesives (SU, Scotchbond Universal and GB, G-[U+04D5]nial Bond) and a two-step self-etch adhesive (OX, OptiBond XTR) were used. The shear bond strength (SBS) and shear fatigue strength (FS) of the enamel and dentin were obtained with and without phosphoric acid pre-etching prior to application of the adhesives. The specimens were stored in distilled water at 37. °C for 24. h, 6 months, and one year. A staircase method was used to determine the FS using a frequency of 10. Hz for 50,000 cycles or until failure occurred. Results: The SBS and FS of enamel bonds were significantly higher with pre-etching, when compared to no pre-etching for the same water storage period. The FS of dentin bonds with pre-etching tended to decrease relative to no pre-etching at the same storage period. For the one year storage period, SU and GB with pre-etching showed significantly lower FS values than the groups without pre-etching. Conclusions: The influence of water storage on FS of the self-etch adhesives was dependent on the adhesive material, storage period and phosphoric acid pre-etching of the bonding site. Clinical significance: Phosphoric acid pre-etching of enamel improves the effectiveness of self-etch adhesive systems. Inadvertent contact of phosphoric acid on dentin appears to reduce the ability of self-etch adhesives to effectively bond resin composite materials.

KW - Fatigue strength

KW - Long-term water storage

KW - Phosphoric acid pre-etching

KW - Self-etch adhesive

UR - http://www.scopus.com/inward/record.url?scp=84949475822&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84949475822&partnerID=8YFLogxK

U2 - 10.1016/j.jdent.2015.10.018

DO - 10.1016/j.jdent.2015.10.018

M3 - Article

JO - Journal of Dentistry

JF - Journal of Dentistry

SN - 0300-5712

ER -